配方类型:

ADHESIVES

配方说明:

Nylon to Nylon (Self-Curing, 2-3 Days)

配方组成:

Magnesium Oxide/4
DuPont "Neozone" A/2
Milling
Litharge, Sulfur and Zinc Oxide/5 minutes
"Neoprene" CG/50
DuPont "Accelerator" 833*/4
R-12 "Neville" Resin/20
Stearic Acid/1
Toluene/480
*To be withheld until cement is ready to be used; "Accelerator" 808 can
be substituted for 833.
Zinc Oxide/5
Litharge/20
"Neoprene" AC/50
Mill Roll Temperature/90-100'F
"Neoprene" mastication time/6 minutes
Sulfur ("Blackbird")/4
"Neozone" A/3 minutes
Magnesium Oxide and Stearic Acid/5 minutes

配制方法:

Mixing: All components with the exception of the R-12 "Neville Resin" are added to the toluene under agitation. The R-12 "Neville" Resin is then added after the rubber compound is in solution.