配方类型:

CEMENT AND RELATED PRODUCTS

配方说明:

Caulking Compounds

配方组成:

Talc/3.50 or 100.00 % by Wt
The caulk was mixed in a sigma blade mixer. "Indopol" Polybutene,
butyl rubber solution and drying oil were added and mixed well (5-10
minutes). Then the fillers were slowly added to the mixing vehicle in
the order shown above. After the addition of titanium-calcium pigment,
the mass was mixed to a smooth paste (about 35 minutes). the drier was
added along with sufficient mineral spirits to obtain the desired
consistency. Mixing was continued until the mass was uniform (about 3-5
minutes).
No.3 (Polybutene
Talc Filler/14.01
Titanium-Calcium Pigment/4.67
Cobalt Drier, 6%/0.03
Blown Soya Oil, Z4 viscosity/5.00 % by Wt
Mineral Spirits/5.66 or 100.00
"Indopol H-1900" Polybutene/20.48
soya Fatty Acid/0.30 % by Wt
Blown Soya Oil, Z2, Z4 viscosity/3.07
"Atomite" filler/46.06
Talc Filler/15.35
Titanium-Calcium Pigment/10.23
Cobalt Drier, 6%/0.03
Mineral Spirits/4.78 or 100.00

配制方法:

The caulk was mixed in a sigma blade mixer. INDOPOL Polybutene and drying oil were added and mixed well (5-10 minutes). Then the fillers were slowly added to the mixing vehicle in the order shown above. After the addition of titanium-calcium pigment, the mass was mixed to a smooth paste (about 35 minutes). the drier was added along with sufficient mineral spirits to obtain the desired consistency. Mixing was continued until the mass was uniform (about 3-5 minutes).