配方类型:

ADHESIVES

配方说明:

Low-Density Polyethylene Hot-Melt Adhesive

配方组成:

Elongation (%)/44
In the laboratory, the components are blended with constant mixing
at 204 C under a nitrogen blanket until the mix is homogeneous.
Test Results
Indopol Polybutene H-100/30
Durometer hardness/58
Wingtack 95/40
Needle penetration (mm)/2.2
T-peel adhesion* (N/m width)
Natural kraft, 60 lb/313.0^t
Indopol Polybutene H-1500/-
Polyethylene Film, untreated/233.1^t
Aluminum foil, 0.0025 in./241.8^t
*Denotes substrate tear
LDPE (155 g/10 min melt index)/40
Wax/20
BHT Andioxidant/1
LDPE (2100 g/10 min melt index)/-
Viscosity @ 149 C (cps)/1550
LDPE (24.5 g/10 min melt index)/-
Softening point ('C)/95
Indopol Polybutene L-14/-
Tensile strength (kPa)/1413

配制方法: