配方类型:

ELASTOMERS, POLYMERS, AND RESINS

配方说明:

Rubber Covering for Rollers

配方组成:

Wax/-
Dutrex 729/4.0
2,2,4-Trimethyl-1,2-Dihydroquinoline (polymerized)/2.0
N-660, GPF Black/-
Zinc 2-Mercaptobenzimidazole/2.0
After air oven aging for 7 days at 100 C
Cure Time at 160 C (min)/17
Hardness, IRHD/49
Caloxol W5G/-
Zinc Oxide/5.0
Tensile Strength (MPa)/24.7
Elongation at Break (%)/605
Novor 924/4.2
300% Modulus (MPa)/5.8
Sulfur/0.4
Relaxed Modulus (MPa)/1.14
Compression Set 70 h at 23 C (%)/7
CBS/-
Compression Set 22 h at 70 C (%)/18
Resilience, Dunlop Tripsometer (%)/85
N-Oxydiethylenebenzothiazole-2-Sulfenamide/0.1
Tension Fatigue, 0-100% strain, Median life (kc)/60
TMTM/-
Tetrabutylthiuram Disulfide/1.5
*Other high quality latex grades of SMR may also be used.
Change in Hardness, IRHD/+2
Change in Tensile Strength (%)/-36
Change in Elongation at Break (%)/-26
Stearic Acid/-
N-762, SRF-LM-NS Black/30.0
Change in 300% Modulus (%)/+39
Tension

配制方法: