配方类型:

METALS AND THEIR TREATMENT

配方说明:

Alkaline Cleaners
Soak or electrolytic

配方组成:

Sodium hydroxide/2 oz/gal*
Operating Conditions: Bath temperature 180-212'F Immersion time
3-10 min. Clean until no water break occurs in rinse.
Comments** For average type soil removal and prior to chemical
treatment and electroplating. In electrolytic cleaning, parts are
cathodic; current density 10-50 amp/ft^2 and 6 volts dc. Use steel
tanks, maintain pH above 11.0.
**Anodic cleaning not recommended; undesirable oxide and hydroxide
surface films will form, and surface pitting may occur from prolonged
cleaning.
*Cleaners containing more than 2% sodium hydroxide (NaOH) will attack
ZK60A, ZK60B and some magnesium-lithium alloys with a resultant decrease
in dimensions.
Formula No.
Sodium carbonate/3 oz/gal*
Sodium hydroxide/2 oz/gal*
Wetting agent/0.1 oz/gal*
Wetting agent/0.1 oz/gal*
Sdoium carbonate/3 oz/gal*
Trisodium phosphate/4 oz/gal*
Sodium Carbonate/4 oz/gal*
Wetting agent/0.1 oz/gal*

配制方法:

Operating Conditions: Bath temperature 180-212'F Immersion time 3-10 min. Clean until no water break occurs in rinse.
Comments** For average type soil removal and prior to chemical treatment and electroplating. In electrolytic cleaning, parts are cathodic; current density 10-50 amp/ft^2 and 6 volts dc. Use steel tanks, maintain pH above 11.0.
**Anodic cleaning not recommended; undesirable oxide and hydroxide surface films will form, and surface pitting may occur from prolonged cleaning.
*Cleaners containing more than 2% sodium hydroxide (NaOH) will attack ZK60A, ZK60B and some magnesium-lithium alloys with a resultant decrease in dimensions.